DESALINATION USING GRAPHENE OXIDE-CELLULOSE COMPOSITE MEMBRANE
No Thumbnail Available
Date
2022
Journal Title
Journal ISSN
Volume Title
Publisher
An Official Publication of Enugu State University of Science & Technology: Journal of Experimental Research SEPTEMBER 2022
Abstract
ABSTRACT
The ion separation potential of graphene oxide-cellulose membrane produced from waste
materials for use in filtration processes is demonstrated in this study. Graphene nanomaterial was
prepared by electrochemical exfoliation of electrodes from waste zinc-carbon batteries and
characterized using TEM, UV-Vis, FTIR, and SEM/EDX techniques. The membrane was
fabricated from graphene oxide and recycled cellulose paper pulp and was also characterized.
The membrane has a surface area of 0.001735 m, and under vacuum pressure of 0.3 Pa was
found to have average permeability of 6.5285 x 10 m/m.s.Pa, flux of 1.9585 x 10 m/m.s, and
volumetric flow rate of 3.3985 x 10 m/s. Membrane desalination studies were performed using
a suction pump set-up for time intervals of 30, 60, 90, 120, and 150min on sodium
chloride–simulated brackish, saline and hyper-saline water. The ion separation efficiency
measured by conductivities of water samples was found at the end of 150 min to be 91.0, 90.89,
and 92.98% for brackish, saline, and hyper-saline water respectively. Optimum ion separation
was obtained in the first 30 min of the desalination experiment (96.95, 96.63 and 96.56% for
brackish, saline, and hyper-saline water respectively), after which there was a progressive
increase in conductivities of all water samples due to swelling of the composite membrane.
Desalination, Membrane, Cellulose, Graphene, Electrochemica