Preparation and Characterization of ZnS Thin Films Grown by Spin Coating Technique
No Thumbnail Available
Date
2020
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
College of Natural and Applied Sciences, University of Dar es Salaam
Abstract
Spin coating technique was used to deposit zinc sulphide (ZnS) thin films successfully onto glass
substrates and the effects of the number of spin times on the optical properties investigated. The
morphology and structures of the prepared thin films were also confirmed. X-ray diffraction
confirmed that spin coated ZnS films exhibited cubic structure, where reflections from (111), (220)
and (311) are clearly visible with a preferential orientation along (111) plane. The calculated
crystallite size for 1S sample from the XRD data is 8.8 nm. From the optical studies, the thin films
exhibit good optical properties with relatively high transmittance (81 %) and low absorbance in the
visible region. The transmittance decreases as the number of spin time increases, and this may be
attributed to increase in thickness of the films. This feature is reflected in all the other optical
parameters. The band gaps obtained ranged from 3.70 to 3.87 eV, which are relatively higher than
the energy band gap of the bulk ZnS material (i.e., 3.65 eV) and it increases with increasing
number of spin times. The SEM micrograph showed that the films deposited are uniform
throughout the surface without voids. EDX analysis showed the presence of zinc and sulphur in
the prepared films with percentages by weights of 78.2% and 6.0%, respectively, showing that the
films are sulphur deficient. These results therefore showed that the prepared ZnS films exhibit
properties of materials that can be used as optoelectronic devices especially as window for
photovoltaic cells.
Description
Keywords
Zinc sulphide thin films, Spin coating technique, Optoelectronic properties, EDX, Surface morphology