Catalytic graphitization of novolac resin for refractory applications

dc.contributor.authorTalabi, Segun Isaac
dc.contributor.authorLuz, Ana Paula
dc.contributor.authorLucas, Alessandra de Almeida
dc.contributor.authorPagliosa, Carlos
dc.contributor.authorPandolfelli, Victor Carlos
dc.description.abstractThis study investigated how to induce graphite generation from the carbonization process of novolac resins using conditions that can be adopted for carbon-containing refractories (CCRs) production. The effect of boron oxide or boric acid (graphitizing agents), cross-linking additive (hexamethylenetetramine) and some processing parameters (mixing technique, vacuum degassing, heating rate and thermal treatments) on carbon graphitization from a commercial novolac resin were evaluated. The X-ray diffraction (XRD) technique was selected to measure the graphitization level and crystal parameters of the prepared samples. Based on the attained results, adding graphitizing agents prior to the pyrolysis of resin resulted in carbon crystallization. The best graphitization level was obtained when the mixtures containing 6 wt% B2O3 or 10 wt% H3BO3 were fired up to 1000 °C for 5 h using a heating rate of 3 °C/min. Although the reproducibility of the obtained results was ascertained, heterogeneous graphitization could be observed based on the XRD profiles, as well as some discrepancies in the calculated graphitization level values. This phenomenon was attributed to the additives susceptibility to agglomeration, preferential graphitization starting from lower binding energy sites and heat treatment temperature, among others.en_US
dc.publisherCeramics International, Elsevieren_US
dc.titleCatalytic graphitization of novolac resin for refractory applicationsen_US

Files in this item


This item appears in the following Collection(s)

Show simple item record